Effect of Nitrogen Content on Microstructural Aspects and Creep Behavior in Extremely Low Carbon 9Cr Heat-resistant Steel
نویسندگان
چکیده
منابع مشابه
the washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests
در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است
15 صفحه اولCreep and Fatigue Interaction Behavior in Sanicro 25 Heat Resistant Austenitic Stainless Steel
Sanicro 25 is a newly developed advanced high strength heat resistant austenitic stainless steel. The material shows good resistance to steam oxidation and flue gas corrosion, and has higher creep rupture strength than other austenitic stainless steels available today. It is thus an excellent candidate for superheaters and reheaters for advanced ultra-super critical power plants with efficiency...
متن کاملeffect of grain size on diffusion of nitrogen in heat treated ck45 plain carbon steel
in this study, the effect of grain size on nitrogen diffusion into ck45 has been investigated. in order to obtain different grain sizes, samples were annealed and normalized at various temperatures and durations.the grain size was determined with clemex vision software. then, the specimens were exposed to dc plasma nitriding treatment and again analyzed by optical microscope ,scanning electron ...
متن کاملEFFECT OF HIGH TEMPERATURE OXIDATION ON THE CORROSION BEHAVIOR OF ALUMINIZED LOW CARBON STEEL IN MOLTEN ALUMINUM
Hot dip aluminizing was carried out on the low carbon steel rod under optimized conditions. The aluminized samples were further oxidized at 1000̊C in air atmosphere at two different times of 20 and 60 minutes. Microstructure study and phase analysis were studied by scanning electron microscopy and X-ray diffraction methods, respectively. The characterization of the coating showed that, Fe2...
متن کاملStatic Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 2004
ISSN: 0915-1559
DOI: 10.2355/isijinternational.44.1243