Effect of Pores on Grain Growth and Grain Boundary Migration in Polycrystalline Magnesia
نویسندگان
چکیده
منابع مشابه
Misorientation Dependence of the Grain Boundary Energy in Magnesia
Geometric and crystallographic data obtained from a well annealed magnesia polycrystal have been used to specify the five macroscopic degrees of freedom for 4665 grain boundaries. The results indicate, that for this sample, the five parameter grain boundary character space is fully occupied. A finite series of symmetrized spherical harmonics has been used to approximate the misorientation depen...
متن کاملGrain growth kinetic of spark plasma sintered magnesia
In this research, the densification of magnesia nanopowder with a mean particle size of about 100 nm was investigated by spark plasma sintering undera pressures of 80 MPa and at temperature range from 1000 °C to 1400 °C and a heating rate of 50 °C/min for 20 minutes. The density of the samples slowly increased with increasing sintering temperatures to 1200 °C. Afterwards, with more increasing o...
متن کاملGRAIN BOUNDARY DIFFUSION IN POLYCRYSTALLINE SILICON FILMS ON SiO2
The enhanced grain boundary diffusion in cw laser processed LPCVD polycrystalline silicon films on insulating SiC>2 has been investigated and the grain boundary diffusion coefficient D' for Phosphorus has been determined. Mesa diodes were fabricated in the large grain poly-Si films by standard photolithographic and etching methods and subsequent ion implantation. The electron beam induced curre...
متن کاملGrain-boundary-induced melting in quenched polycrystalline monolayers.
Melting in two dimensions can successfully be explained with the Kosterlitz-Thouless-Halperin-Nelson-Young (KTHNY) scenario which describes the formation of the high-symmetry phase with the thermal activation of topological defects within an (ideally) infinite monodomain. With all state variables being well defined, it should hold also as freezing scenario where oppositely charged topological d...
متن کاملEffect of Grain-Boundary Phase
Two types of hot-pressed silicon nitride, one having an amorphous grain-boundary phase (6 wt% yttria, 3 wt% alumina) and the other having a predominantly crystalline grain-boundary phase (8 wt% yttria, 1 wt% alumina), were tested on a split Hopkinson pressure bar with a momentum trap, such that, in each test, the sample was subjected to a single predefined stress pulse and then recovered withou...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Association, Japan
سال: 1977
ISSN: 0009-0255,1884-2127
DOI: 10.2109/jcersj1950.85.984_390