Effect of Thermomechanical Treatment on the Mechanical Properties of 316L Stainless Steel
نویسندگان
چکیده
منابع مشابه
Effect of Thermomechanical Processing on the Microstructure and Mechanical Properties of a Duplex Stainless Steel
Duplex stainless steels (DSSS) have a microstructure composed of ferrite and austenite phases that gives them a very good combination of mechanical and corrosion properties. These steels are desirable for many applications in the chemical and petrochemical industries. In the present study, a type of stainless steel was cast, solution annealed at 1200°C for 60 min and then quenched in water. Ini...
متن کاملAn Investigation on Mechanical Properties of Ultrafine Grained 316 Stainless Steel by Thermomechanical Treatment
In this paper, an advanced thermo-mechanical treatment was conducted on AISI 316 austenitic stainless steel. At first, three samples were rolled at the ambient temperature, the temperature of -20 ºC (dry ice and ethanol) and -196 ºC (liquid nitrogen). Then, the samples were annealed at 800 ºC in the time range of 1 to 15 minutes. In each step, the microhardness values of the samples were measur...
متن کاملThe Effect of Surface Treatment on Corrosion behavior of Surgical 316L Stainless Steel Implant
The AISI 316 L Stainless Steel (SS) specimens were exposed to passivation surface through two different processes including; holding in 40-vol% HNO3 at temperature of 60 ºC for 30 min and 15-vol%H2SO4 at ambient temperature for 1 hour. The corrosion behavior of specimens was evaluated in physiological solutions by electrochemical in vitro tests through linear an...
متن کاملEvaluation of microstructure and mechanical properties of friction stir welded copper / 316L stainless steel dissimilar metals
In the present research, friction stir welding (FSW) process was used for butt joining of pure copper plate to 316L stainless steel plate. Mechanical properties and microstructural characteristics of the joint were evaluated by microhardness and tensile tests as well as optical and scanning electron microscope (SEM). It was found that microstructure of the weld nugget (WN) has fine grains where...
متن کاملThe Effect of Tempering Treatment on the Microstructure and Mechanical Properties of DIN 1.4021 Martensitic Stainless Steel
To investigate the effect of tempering treatment on mechanical properties and the microstructure of DIN 1.4021 Martensitic Stainless Steel, austenite treatment was conducted for the samples at 1000 ºC temperature for 60 min and then the samples were oil quenched. Later, tempering treatments were performed for the samples at 500 ºC and 700 ºC temperatures for 2 and 5 h, respectively; then quench...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Korea Society For Power System Engineering
سال: 2014
ISSN: 1226-7813
DOI: 10.9726/kspse.2014.18.3.100