Elastic-plastic fatigue creack growth characteristics and fracture mechanics parameters in A508-3 steel.
نویسندگان
چکیده
منابع مشابه
The Fracture Mechanics Concept of Creep and Creep/Fatigue Crack Growth in Life Assessment
There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...
متن کاملFatigue Failure of Structural Steel – Analysis Using Fracture Mechanics
Fatigue is the major threat in service of steel structure subjected to fluctuating loads. With the additional effect of corrosion and presence of weld joints the fatigue failure may become more critical in structural steel. One of the apt examples of such structural is the sailing ship. This is experiencing a constant stress due to floating and a pulsating bending load due to the waves. This pa...
متن کاملNumerical Estimation of Fracture Parameters in Elastic and Elastic-plastic Analysis
The finite element method has been largely used to analyze mechanical problems and, in particular, to obtain the response of cracked structures. One of the major issues in using the method is mesh generation. Nowadays, several automatic mesh generation algorithms are available for two-dimensional models. Crack analysis imposes severe requirements on automatic mesh generation. It is not uncommon...
متن کاملFracture Mechanics and Corrosion Fatigue
The development and current state-of-the-art in fracture mechanics in relation to studies of environment-enhanced fatigue-crack growth (corrosion fatigue) and fatigue-crack growth per se are reviewed. Patterns of response of materials to different loading and environmental conditions are considered in terms of the probable mechanisms for environmental embrittlement. The usefulness of the fractu...
متن کاملFracture toughness and fatigue crack growth characteristics of nanotwinned copper
Recent studies have shown that nanotwinned copper (NT Cu) exhibits a combination of high strength and moderate ductility. However, most engineering and structural applications would also require materials to have superior fracture toughness and prolonged subcritical fatigue crack growth life. The current study investigates the effect of twin density on the crack initiation toughness and stable ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1985
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.51.2441