Electrical promotion-assisted automotive exhaust catalyst: highly active and selective NO reduction to N2 at low-temperatures
نویسندگان
چکیده
Low-temperature operation of TWC can be achieved even at 423 K by applying an electric field to the semiconductor catalyst.
منابع مشابه
Selective Catalytic Reduction of No Byc3h6 over a Commercial Automotive Iridium Based Catalyst
Ir/TiO2 coated on cordierite monolith was investigated in the selective catalytic reduction (SCR) of NO with propene using a broad temperature range and simulated diesel exhaust gas conditions under the standard mixture (1000 vpm NO, 2000 vpm C3H6, 500 vpm CO, 10 vol.% O2). The physicochemical characterization of the commercial catalyst showed that the BET surface area of the fresh and aged sam...
متن کاملHighly selective catalytic reduction of NO via SO2/H2O-tolerant spinel catalysts at low temperature
Selective catalytic reduction of NO X by hydrogen (H2-SCR) in the presence of oxygen has been investigated over the NiCo2O4 and Pd-doped NiCo2O4 catalysts under varying conditions. The catalysts were prepared by a sol-gel method in the presence of oxygen within 50-350 °C and were characterized using XRD, BET, EDS, XPS, Raman, H2-TPR, and NH3-TPD analysis. The results demonstrated that the doped...
متن کاملMicrowave-assisted deposition of a highly active cobalt catalyst on mesoporous silica for photochemical CO2 reduction.
Coupling with robust surfaces is a promising approach to improve the stability and recyclability of highly active molecular catalysts. This study builds on our prior success to deposit a Co(iii) cyclam complex, where cyclam is 1,4,8,11-tetraazacyclotetradecane, on mesoporous silica via a microwave-assisted process. The Co(iii) complex was successfully deposited on the silica surface through rea...
متن کاملSticking coefficient of nitrogen on solid N2 at low temperatures
The sticking coefficient of nitrogen gas on a thick solid nitrogen film on a copper cold finger was studied at low temperature. For surface temperatures of about 12 K the sticking coefficient is measured to be 99.0 0.6%. Our result implies that it will be possible to make a intense and high brightness slow positron source starting from a small diameter deposit of the gaseous positron emitter N2...
متن کاملIron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3.
The catalysts of iron-doped Mn-Ce/TiO2 (Fe-Mn-Ce/TiO2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction (SCR) of NO with NH3. It was found that the NO conversion over Fe-Mn-Ce/TiO2 was obviously improved after iron doping compared with that over Mn-Ce/TiO2. Fe-Mn-Ce/TiO2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity. The results...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Catalysis Science & Technology
سال: 2021
ISSN: ['2044-4761', '2044-4753']
DOI: https://doi.org/10.1039/d1cy00591j