Electrical Resistance Characteristics in Wet CFRP Cross-Ply Laminates with Matrix Cracking
نویسندگان
چکیده
منابع مشابه
Failure Criterion for Two-Ply Plain-Weave CFRP Laminates
We present an experimentally-based failure criterion for symmetric two-ply plain-weave laminates of carbon-fiber reinforced plastic. The criterion is formulated in terms of six force and moment stress resultants and consists of a set of three inequalities, related to in-plane, bending, and combined in-plane and bending types of failure. All failure parameters in the criterion are measured direc...
متن کاملPropagation of Matrix Cracking and Induced Delaminatin in Cross-Ply Composite Beams Subjected to Bending Loads
Due to the mismatch of mechanical properties in composite laminates, propagation of delami-nation is considered as a severe damage mechanism in beams with various lay-up configurations. Delamination can be generated due to matrix cracking propagation or it can also be initiated due to the manufacturing process before using composite beams. Using a micromechanics model, this study is aimed to in...
متن کاملPost-cure shape errors of ultra-thin symmetric CFRP laminates: Effect of ply-level imperfections
This paper discusses the effect of misalignments in ply orientation, uniform variations in ply thickness, and through-thickness thermal gradients on the post-cure shape errors for symmetric cross-ply laminates constructed from ultra-thin composite materials. Photogrammetry-based surface measurements are performed for laminates cured at elevated temperatures. Significant out-of-plane shape error...
متن کاملOn the Effect of Residual Stresses on the Transverse Cracking in Cross-ply Carbon-polyetherimide Laminates Proefschrift
Two themes form the basis of this study on fibre reinforced laminated composites: namely 'thermal residual stress' and 'transverse cracking'. Thermal residual stresses are inherent to any composite structure and are internal stress within the structure that form during manufacture. Their formation arises from the difference in coefficient of thermal expansion of the fibre and the matrix. These ...
متن کاملThe Formation and Effect of Outer-Ply Microcracks in Cross-Ply Laminates: A Variational Approach
The microcracking process in laminates which have outer-ply 90◦ plies (e.g. [90m/0n]s) has some important differences from the microcracking process in laminates which lack outer-ply 90◦ plies (e.g. [0n/90m]s). Foremost among the differences is the characteristic damage state. [90m/0n]s laminates form antisymmetric or staggered microcracks while [0n/90m]s laminates form symmetric microcracks. T...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society for Composite Materials
سال: 2011
ISSN: 0385-2563,1884-8559
DOI: 10.6089/jscm.37.226