Electrochemical property of Al-Si alloy brazing filler.
نویسندگان
چکیده
منابع مشابه
Vacuum Brazing of Zirconium-Based Alloy and 321 Stainless Steel Using Titanium Based Filler Metal
Both Zirconium-based alloys and 321stainless steel are widely used as engineering alloys due to their good mechanical properties. Conventional fusion welding techniques for Zr alloys and stainless steel are not feasible due to the formation of brittle intermetallic compounds such as (Zr3Fe, ZrFe2 and Zr2Fe) and corrosion cracking. Brazing is one of the most wide...
متن کاملInvestigation on effect of holding time in brazing of steel to cemented carbide using Cu-Ag alloy filler metal
Nowadays, cemented carbides-steels joints by brazing method are taken into consideration. One of the problems of these joints is the creation residual stresses that can reduce it with choose correct parameters of brazing. In this study, Silver base alloy filler containing copper, zinc and cadmium have been used in temperature 780°C and the effect of time parameter 5, 10 and 15 minutes on micros...
متن کاملWettability of Brazing Filler Metals on Copper and Copper Alloys
The possibility of alloying can not be avoided at the interface between molten brazing filler metal and base metal in brazing, so the wettability of brazing filler metal can not be easily explained theoretically. We used the original apparatus for wettability test and investigated the relation between the wettability of brazing filler metals of Ag-P-Cu and Ag-Cu-Zn-Cd systems on copper and the ...
متن کاملInvestigation on effect of holding time in brazing of steel to cemented carbide using Cu-Ag alloy filler metal
Nowadays, cemented carbides-steels joints by brazing method are taken into consideration. One of the problems of these joints is the creation residual stresses that can reduce it with choose correct parameters of brazing. In this study, Silver base alloy filler containing copper, zinc and cadmium have been used in temperature 780°C and the effect of time parameter 5, 10 and 15 minutes on micros...
متن کاملEffect of Al–5Ti–C Master Alloy on the Microstructure and Mechanical Properties of Hypereutectic Al–20%Si Alloy
Al-5Ti-C master alloy was prepared and used to modify hypereutectic Al-20%Si alloy. The microstructure evolution and mechanical properties of hypereutectic Al-20%Si alloy with Al-5Ti-C master alloy additions (0, 0.4, 0.6, 1.0, 1.6 and 2.0 wt%) were investigated. The results show that, Al-5Ti-C master alloy (0.6 wt%, 10 min) can significantly refine both eutectic and primary Si of hypereutectic ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1996
ISSN: 0451-5994,1880-8018
DOI: 10.2464/jilm.46.113