Ellipsometric Evaluation of the Optical Constants of Zirconium Oxynitride Thin Films Deposited by Reactive Pulsed Magnetron Sputtering
نویسندگان
چکیده
منابع مشابه
AlNXOY THIN FILMS DEPOSITED BY DC REACTIVE MAGNETRON SPUTTERING
AlNxOy thin films were produced by DC reactive magnetron sputtering, using an atmosphere of argon and a reactive gas mixture of nitrogen and oxygen, for a wide range of partial pressures of reactive gas. During the deposition, the discharge current was kept constant and the discharge parameters were monitored. The deposition rate, chemical composition, morphology, structure and electrical resis...
متن کاملDevelopment of Zirconium Thin Films by Pulsed Direct Current Magnetron Sputtering: Effect of Pulsed Parameters
This paper characterizes phases present in thin Zr films at 773 K of substrate temperature. The effect of pulsed parameters such as pulse frequency, duty cycle and pulse power during the deposition of Zr film on Si(100) at the substrate temperature of 773 K has been studied. Formation of α-phase of zirconium was noticed with (001) preferred orientation at 773 K. Preferred orientation was found ...
متن کاملOptical constants of crystalline WO3 deposited by magnetron sputtering
constants of crystalline WO 3 deposited by magnetron sputtering" (1999). Crystalline WO 3Ϫx is an infrared ͑IR͒ electrochromic material having possible applications in satellite thermal control and IR switches. Optical constants of electrochromic materials change upon ion intercalation, usually with H ϩ or Li ϩ. Of primary concern for device design are the optical constants in both the intercalat...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کاملSuperhard NbB2-x thin films deposited by dc magnetron sputtering
We have deposited weakly textured substoichiometric NbB2-x thin films by magnetron sputtering from a NbB2 target. The films exhibit superhardness (42 ± 4 GPa), previously only observed in overstoichiometric TiB2 thin films, and explained by a self-organized nanostructuring, where thin TiB2 columnar grains hinder nucleation and slip of dislocations and a B-rich tissue phase between the grains pr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Physica Polonica A
سال: 2013
ISSN: 0587-4246,1898-794X
DOI: 10.12693/aphyspola.124.141