Enhanced elevated-temperature properties via Mo addition in Al-Mn-Mg 3004 alloy
نویسندگان
چکیده
منابع مشابه
Microstructures and Properties Evolution of Al-Cu-Mn Alloy with Addition of Vanadium
The effect of the vanadium addition on the microstructure, the precipitation behavior, and the mechanical properties of the Al-5.0Cu-0.4Mn alloy has been studied. The as-cast Al-5.0Cu-0.4Mn alloy was produced by squeeze casting and the heat treatment was carried out following the standard T6 treatment. It is shown that, with the addition of V, grain refinement of aluminum occurred. During heat ...
متن کاملInfluence of Rolling Temperature on Microstructure and Mechanical Properties of Cryorolled Al-Mg-Si Alloy
An effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy was studied. The material was rolled up to a true strain of ∼0.7 at three different temperatures viz; room temperature, liquid propanol and liquid nitrogen. The liquid nitrogen rolled sample exhibited superior properties with a yield and tensile strength of 332 MPa and 364 MPa, respe...
متن کاملFRACTIONAL RECRYSTALLIZATION KINETICS IN DIRECTLY COLD ROLLED Al-Mg, Al-Mg-Sc AND Al-Mg-Sc-Zr ALLOY
The evaluation of texture as a function of recrystallization has been characterized for directly cold rolled Al-6Mg, Al-6Mg-0.4Sc and Al-6Mg-0.4Sc-0.2Zr alloys. Samples were annealed isothermally at 400 °C for 1 to 240 minutes to allow recrystallization. Recrystallization kinetics of the alloys is analyzed from the micro-hardness variation. Isothermally annealed samples of aluminum alloys were ...
متن کاملDsc Study of Precipitation in an Al-mg-mn Alloy Microalloyed with Cu
Power compensation DSC has been employed to detect and analyse precipitation reactions in an Al1.3Mg-0.4Mn and an Al-1.3Mg-0.4Mn-0.07Cu alloy in which very small amounts of precipitate, less than 0.3 at%, are expected to form. Due to the very small heat effects, baseline instability and drift significantly interfere with the measurements. After repeated experiments and careful baseline correcti...
متن کاملProperties of Low-alloy High-speed Steel at Elevated Temperature
J. Jaworski, T. Trzepieciński: Faculty of Mechanical Engineering and Aeronautics, Rzeszow University of Technology, Rzeszów, Poland This paper presents the results of research on the determination of the coefficient of thermal conductivity and hot hardness of cutters made of selected grades of low-alloy high-speed steels, HS 6-5-2 and HS3-1-2. The investigations of hot hardness and yield stress...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Alloys and Compounds
سال: 2017
ISSN: 0925-8388
DOI: 10.1016/j.jallcom.2016.10.005