Enhancing lithium leaching by mechanical activation
نویسندگان
چکیده
منابع مشابه
Enhancing Mechanical Strength of Inorganic Geopolymer by Using Phenol Resin
The effect of organic phenol on the compressive and flexural strength of a metakaolin based geopolymer is studied. It was found that 12 wt% phenol resins can increase the compressive and flexural strength by 30% and 65% respectively. In addition, the reinforcing effect of phenol resin is higher in Na-PS and Na-PSS type geopolymers rather than Na-PSDS. Two distinct endothermic peaks were detecte...
متن کاملThe Influence of Mechanical Activation of Chalcopyrite on the Selective Leaching of Copper by Sulphuric Acid
Base metal sulphides are an important source of various metals. They are typically intergrowth and due to the complex nature of their ores, the hydrometallurgical technique is the very convenient way of extracting the desired component. If it is possible to extract the metal from an ore selectively, the subsequent processing steps become less complicated. Mechanical activation seems to be a fav...
متن کاملEffect of Mechanical Activation on the Kinetics of Ammoniacal Thiosulfate Leaching of a Refractory Oxide Gold Ore
The effect of mechanical activation on the kinetics of ammoniacal thiosulfate leaching of a refractory oxide gold ore containing 2.8 ppm Au was investigated. The gold extraction of 99.81% was achieved by 16 h leaching of a sample mechanically activated for 60 minutes. The gold extraction observed for a similar reference sample without mechanical activation was only 55%. Studies revealed that le...
متن کاملStudying ilmenite dissolution using mechanical activation method
In this work, the effects of temperature, acid concentration, and mechanical activation on dissolution of ilmenite were studied using the statistical design of experiment technique. Mechanical activation was carried out using a planetary ball mill in dry mode, and the resulting structural changes were characterized by the particle size analysis, specific surface area measurements, and X-ray dif...
متن کاملExtraction of Lithium from Lepidolite Using Mixed Grinding with Sodium Sulfide Followed by Water Leaching
Mixed grinding with Na2S followed by water leaching was performed to extract Li from lepidolite. The leachability of Li increases dramatically in the ground mixture, regardless of the mixing ratio over the range of 1:1 to 3:1, while only 4.53% of Li was extracted in lepidolite ground without Na2S. The leachability increased with an increase of the grinding time, and ultimately, 93% of the Li wa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Mongolian Journal of Chemistry
سال: 2018
ISSN: 2414-0082,2226-6739
DOI: 10.5564/mjc.v19i45.1090