Estimating Method for Fatigue Crack Growth under Narrow Band Random Loading
نویسندگان
چکیده
منابع مشابه
Fatigue crack growth characteristics of Fe and Ni under cyclic loading using a quasi-continuum method
A quasi-continuum (QC) method based on the embedded atom method (EAM) potential was employed to investigate the fatigue crack growth and expansion characteristics of single-crystal Fe and Ni under cyclic loading modes I and II. In particular, the crack growth and expansion characteristics of Fe and Ni under cyclic loading were evaluated in terms of atomic stress fields and force–distance curves...
متن کاملPrediction of Crack Initiation Direction for Inclined Crack Under Biaxial Loading by Finite Element Method
This paper presents a simple method based on strain energy density criterion to study the crack initiation angle by finite element method under biaxial loading condition. The crack surface relative displacement method is used to eliminate the calculation of the stress intensity factors which are normally required. The analysis is performed using higher order four node quadrilateral element. The...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملA Dynamical Coefficient Mechanics Model for Fatigue Crack Growth under Constant Amplitude Loading
Almost all load bearing components usually experience variable amplitude loading (VAL) rather than constant amplitude loading (CAL) during their service lives. Although many models have been proposed on this subject, but life prediction under these complex situations is still under constant improvement. The present study aims at evaluating residual fatigue life under CAL due to application of t...
متن کاملFatigue of polycrystalline silicon for microelectromechanical system applications: crack growth and stability under resonant loading conditions
Although bulk silicon is not known to exhibit susceptibility to cyclic fatigue, micron-scale structures made from silicon films are known to be vulnerable to degradation by fatigue in ambient air environments, a phenomenon that has been recently modeled in terms of a mechanism of sequential oxidation and stress-corrosion cracking of the native oxide layer. To date, most stress-life (S=N ) fatig...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Naval Architects of Japan
سال: 1987
ISSN: 1884-2070,0514-8499
DOI: 10.2534/jjasnaoe1968.1987.162_467