Estimation of Stress Corrosion Cracking Initiation and Propagation in High-Pressure, High-Temperature Water Environment Utilizing Acoustic Emission
نویسندگان
چکیده
منابع مشابه
Acoustic Emission during Stress Corrosion Cracking Test
AE monitoring from various types of stress corrosion cracking (SCC) has been conducted for the past 15 years in our laboratory. This paper discusses AE results of active-path dissolution-type SCC of austenitic stainless steel in chloride solution and fused salt, fluoride and polythionic acid solutions, brass in ammonia (Mattosson's solution), and carbon steels in nitrite solution. Transgranular...
متن کاملNitrogen and Water in High Temperature Corrosion
Service life-time of alloys used in high temperature applications is often limited by corrosion. FeCrAl(Re) alloys are partially designed to form a protective α-alumina oxide scale at elevated temperatures in order to mitigate further oxidation. The scale growth commonly follows a parabolic rate law, which under a Wagnerian setting depends on transport of charged species; ions, vacancies and el...
متن کاملStress- Corrosion Crack Initiation of High-strength Pipeline Steel in Near-neutral pH Environments
Stress-corrosion cracking (SCC) tests were conducted in the near-neutral pH standard solution, NS4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. Pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...
متن کاملAn Outrun Competition of Corrosion Fatigue and Stress Corrosion Cracking on Crack Initiation in a Compressor Blade
First row rotating blades of four axial-flow compressors were prematurely fractured. Previous investigations showed that the site atmosphere contains corrosive compounds which lead to an increase in possibility of pitting on the blades. It was also revealed that the crack was originated from two corrosion pits. Thus, this work is conducted to ascertain which of fatigue or stress corrosion crack...
متن کاملAn Investigation on Corrosion and Stress Corrosion Cracking initiation of a Ferritic Stainless Steel in a Tertiary Amine Solution
The present study focused on stress corrosion cracking (SCC) and corrosion behavior of ferritic stainless steel (grade 430) in activated methyl diethanolamine (aMDEA) solution, which is classified as a tertiary amine. In this regard, cyclic polarization and U-bend tests were performed in CO2 loaded aMDEA with different concentrations at 25 and 70 °C to observe corrosion behavior and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2015
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.m2014357