Evaluating Hydrogen Stress Cracking of Line Pipe Steels under Cathodic Protection Using Crack Tip Opening Displacement Tests.
نویسندگان
چکیده
منابع مشابه
Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging
0010-938X/$ see front matter 2011 Elsevier Ltd. A doi:10.1016/j.corsci.2011.03.028 ⇑ Corresponding author at: Surface Science Wester Ontario, London, Ontario, Canada N6G 0J3. Tel.: +1 51 3709. E-mail address: [email protected] (S. Ramamurth Stress corrosion cracking (SCC) of as-quenched 4340 and 3.5NiCrMoV steels was studied under hydrogen charging conditions, with a cathodic current applied to t...
متن کاملAn Electrochemical Measurement for Evaluating the Cathodic Disbondment of Buried Pipeline Coatings under Cathodic Protection
Steel pipelines are susceptible to corrosion by the action of corrosive substance in the environment and one of the most common failure modes in buried pipeline coatingis cathodic disbondment. Consequently, Electrochemical Impedance Spectroscopy (EIS) was used to assess the effect of three important parameters, the thickness of coating, the artificial defect ...
متن کاملan electrochemical measurement for evaluating the cathodic disbondment of buried pipeline coatings under cathodic protection
steel pipelines are susceptible to corrosion by the action of corrosive substance in the environment and one of the most common failure modes in buried pipeline coatingis cathodic disbondment. consequently, electrochemical impedance spectroscopy (eis) was used to assess the effect of three important parameters, the thickness of coating, the artificial defect and electrolyte type, on cathodic di...
متن کاملA Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels
The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: JSME International Journal Series A
سال: 2001
ISSN: 1344-7912,1347-5363
DOI: 10.1299/jsmea.44.309