Experimental Characterization of Transverse Crack Behavior in High Temperature CFRP Laminates.

CHARACTERIZATION OF TRANSVERSE CRACK AND CRACK GROWTH IN A RAILWAY RAIL

Abstract: To ensure the rail transportations safety, evaluation of fatigue behavior of the rail steel is necessary. High cycle fatigue behaviour of a rail steel was the subject of investigation in this research using fracture mechanics. Finite element method (FEM) was used for analyzing the distribution of the stresses on the rail, exerted by the external load. FEM analysis showed that the ...

Electromagnetic Shielding Property of Cfrp Composite Laminates

Investigation on Flexural Performance of RC Beams Flexurally Strengthened by Side-bonded CFRP Laminates

It is an effective way to improve the flexural behavior of reinforced concrete (RC) members by externally bonded carbon fiber reinforcement polymer (CFRP) laminates on the soffit of the members. However, there is little investigation on flexural performance of RC beam flexurally strengthened by side-bonded FRP laminates. To investigate the flexural behavior of RC beams side-bonded CFRP laminate...

Impact Damage Detection of Toughened CFRP Laminates with Time Domain

Laminated Carbon Fiber Reinforced Polymer (CFRP) composites are very effective in weight saving in aeronautical structural components. For these laminated CFRP structures, it is, however, difficult to detect damage such as delamination, matrix cracks, and local fiber breakages caused by low velocity impact loading In the previous study in 2009, Time Domain Reflectometry (TDR) method was applied...

High Temperature Behavior of Dual Phase Steels

Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...