Facile Synthesis of Carbon Nanosphere/NiCo2O4 Core-shell Sub-microspheres for High Performance Supercapacitor
نویسندگان
چکیده
منابع مشابه
Facile Synthesis of Carbon Nanosphere/NiCo2O4 Core-shell Sub-microspheres for High Performance Supercapacitor
This paper introduced a process to prepare the carbon nanosphere (CNS)/NiCo2O4 core-shell sub-microspheres. That is: 1) CNSs were firstly prepared via a simple hydrothermal method; 2) a layer of NiCo2O4 precursor was coated on the CNS surface; 3) finally the composite was annealed at 350 °C for 2 hours in the air, and the CNS/NiCo2O4 core-shell sub-microspheres were obtained. This core-shell su...
متن کاملCo3O4@CoS Core-Shell Nanosheets on Carbon Cloth for High Performance Supercapacitor Electrodes
In this work, a two-step electrodeposition strategy is developed for the synthesis of core-shell Co₃O₄@CoS nanosheet arrays on carbon cloth (CC) for supercapacitor applications. Porous Co₃O₄ nanosheet arrays are first directly grown on CC by electrodeposition, followed by the coating of a thin layer of CoS on the surface of Co₃O₄ nanosheets via the secondary electrodeposition. The morphology co...
متن کاملNitrogen-doped amorphous carbon-silicon core-shell structures for high-power supercapacitor electrodes
We report successful deposition of nitrogen-doped amorphous carbon films to realize high-power core-shell supercapacitor electrodes. A catalyst-free method is proposed to deposit large-area stable, highly conformal and highly conductive nitrogen-doped amorphous carbon (a-C:N) films by means of a direct-current plasma enhanced chemical vapor deposition technique (DC-PECVD). This approach exploit...
متن کاملEasy synthesis of hollow core, bimodal mesoporous shell carbon nanospheres and their application in supercapacitor.
Hollow core, mesoporous shell carbon nanospheres (HCMSs) with large bimodal mesopores (6.4 and 3.1 nm) and high surface area (1704 m(2) g(-1)) have been synthesized by a triconstituent surface co-assembly of monodisperse silica nanospheres method. The resulted HCMS show a high specific capacity of 251 F g(-1) at 50 mV s(-1) in 2 M H(2)SO(4) and long cyclic life.
متن کاملFacile Synthesis of Free-Standing NiO/MnO2 Core-Shell Nanoflakes on Carbon Cloth for Flexible Supercapacitors
Free-standing NiO/MnO2 core-shell nanoflake structure was deposited on flexible carbon cloth (CC) used as electrode for high-performance supercapacitor (SC). The NiO core was grown directly on CC by hydrothermal process and the following annealing treatment. MnO2 thin film was then covered on NiO structures via a self-limiting process in aqueous solution of 0.5 M KMnO4 and 0.5 M Na2SO4 with a c...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2015
ISSN: 2045-2322
DOI: 10.1038/srep12903