Facile synthesis of core–shell porous Fe 3 O 4 @carbon microspheres with high lithium storage performance
نویسندگان
چکیده
منابع مشابه
Facile Synthesis of Coaxial CNTs/MnOx-Carbon Hybrid Nanofibers and Their Greatly Enhanced Lithium Storage Performance.
Carbon nanotubes (CNTs)/MnOx-Carbon hybrid nanofibers have been successfully synthesized by the combination of a liquid chemical redox reaction (LCRR) and a subsequent carbonization heat treatment. The nanostructures exhibit a unique one-dimensional core/shell architecture, with one-dimensional CNTs encapsulated inside and a MnOx-carbon composite nanoparticle layer on the outside. The particula...
متن کاملAdditive-free synthesis of 3D porous V2O5 hierarchical microspheres with enhanced lithium storage properties
A facile synthesis of novel 3D porous V2O5 hierarchical microspheres has been developed, based on an additive-free solvothermal method and subsequent calcination. Due to their unique structure, these V2O5 microspheres display a very stable capacity retention of 130 mA h g (1) over 100 cycles at a current rate of 0.5 C, and show excellent rate capability with a capacity of 105 mA h g (1) even at...
متن کاملCarbon-coated Fe3O4 microspheres with a porous multideck-cage structure for highly reversible lithium storage.
A novel H3PO4 etching strategy together with subsequent carbon coating has been developed for the synthesis of carbon-coated Fe3O4 microspheres with a porous multideck-cage structure. These carbon-coated Fe3O4 microspheres manifest high specific capacity (∼1100 m h g(-1) at 200 mA g(-1)) and excellent cycling stability for lithium storage.
متن کاملFacile Synthesis of Carbon Nanosphere/NiCo2O4 Core-shell Sub-microspheres for High Performance Supercapacitor
This paper introduced a process to prepare the carbon nanosphere (CNS)/NiCo2O4 core-shell sub-microspheres. That is: 1) CNSs were firstly prepared via a simple hydrothermal method; 2) a layer of NiCo2O4 precursor was coated on the CNS surface; 3) finally the composite was annealed at 350 °C for 2 hours in the air, and the CNS/NiCo2O4 core-shell sub-microspheres were obtained. This core-shell su...
متن کاملA facile method to fabricate carbon-encapsulated Fe(3)O(4) core/shell composites.
One-step synthesis of carbon-encapsulated Fe(3)O(4) core/shell composites is reported. The Fe(3)O(4) cores were formed via the reduction of Fe(3+) by glucose under alkaline conditions obtained by the decomposition of urea. The amorphous carbon shells were carbonized from glucose. A possible formation mechanism for the Fe(3)O(4)@C composite was discussed. In order to characterize these Fe(3)O(4)...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Comptes Rendus. Chimie
سال: 2020
ISSN: 1878-1543
DOI: 10.5802/crchim.18