Facilitating the occurrence of dynamic recrystallization in plain extra low-carbon steel by warm asymmetric rolling

The occurrence of dynamic recrystallization in warm rolling plain extra-low carbon steel was examined by applying 75% thickness reduction a single pass. investigated temperature range ambient to 700 °C. Results show apparently remains absent symmetric below 600 Nevertheless, not only just occurs but accelerates as the condition changed from asymmetric condition. analysis grain internal disorientations and geometrically necessary dislocation densities High-angular Resolution on-axis Transmission Kikuchi Diffraction (HR-TKD) allowed identify type its evolution through range. New grains formed either continuous or discontinuous are preferentially orientated according typical shear texture up °C case rolling. Above °C, dynamically recrystallized produce restrengthening well overall texture.