Fatigue and Fretting Fatigue of Austenitic and Ferritic Stainless Steels in Pseudo-Body Fluid
نویسندگان
چکیده
منابع مشابه
Thermal Fatigue Behavior of 400 Series Ferritic Stainless Steels
In this study, thermal fatigue properties of 400 series ferritic stainless steels have been evaluated in the temperature ranges of 200-800C and 200-900C. Systematic methods for control of temperatures within the predetermined range and measurement of load applied to specimens as a function of temperature during thermal cycles have been established. Thermal fatigue tests were conducted under ful...
متن کاملFretting fatigue behaviour of Ni-free high-nitrogen stainless steel in a simulated body fluid
Fretting fatigue behaviour of Ni-free high-nitrogen steel (HNS) with a yield strength of about 800 MPa, which was prepared by nitrogen gas pressurized electroslag remelting, was studied in air and in phosphate-buffered saline (PBS(-)). For comparison, fretting fatigue behaviour of cold-rolled SUS316L steel (SUS316L(CR)) with similar yield strength was examined. The plain fatigue limit of HNS wa...
متن کاملHydrogen-Induced Delayed Cracking in TRIP-Aided Lean-Alloyed Ferritic-Austenitic Stainless Steels
Susceptibility of three lean-alloyed ferritic-austenitic stainless steels to hydrogen-induced delayed cracking was examined, concentrating on internal hydrogen contained in the materials after production operations. The aim was to study the role of strain-induced austenite to martensite transformation in the delayed cracking susceptibility. According to the conducted deep drawing tests and cons...
متن کاملFatigue behavior of Austenitic Type 316L Stainless Steel
The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...
متن کاملLow-Temperature Carburization of Austenitic Stainless Steels
LOW-TEMPERATURE CARBURIZATION is a gaseous carburization process performed at atmospheric pressure, at temperatures where the kinetics of substitutional diffusion are very slow. Low-temperature carburization hardens the surface of austenitic stainless steels through the diffusion of interstitial carbon, without the formation of carbides. The surface must be activated, by modification and remova...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1999
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.63.12_1600