Fatigue behavior of the 3D orthogonal carbon/glass fibers hybrid composite under three-point bending load
نویسندگان
چکیده
منابع مشابه
Bending fatigue of hybrid composite rods
The flexural fatigue behavior of hybrid composite rods comprised of unidirectional carbon and glass fibers was investigated. Damage was evaluated by monitoring stiffness loss as a function of cycles, and bending fatigue failure was defined in terms of strength retention. The acoustic emission technique and microscopic examination were used to characterize damage progression and failure mechanis...
متن کاملA Clamped Three-point Bending Setup for Fatigue of Thin Composite Laminates
Usually, fatigue tests on fibre-reinforced composites are performed in uni-axial tension/tension or tension/compression fatigue [1], providing the S-N data. Although bending fatigue tests are not widely accepted as a standard, they are used a lot for research purposes [2] and they do have some important advantages [3]. In case of three-point bending fatigue, the history of bending force versus ...
متن کاملCorrosion Fatigue Studies on a Bulk Glassy Zr-Based Alloy under Three-Point Bending
Corrosion fatigue (CF) tests were carried out on bulk glassy Zr52.5Cu17.9Al10Ni14.6Ti5 (Vitreloy 105) samples under load-controlled three-point bending conditions with a load ratio of R = 0.1 in 0.01 M Na2SO4 + 0.01 M NaCl electrolyte. During cyclic testing, the bar-shaped specimens were polarized in situ at constant potentials and the current was monitored. Three different anodic potentials wi...
متن کاملan inverstigation into the shrinkage behavior (kinetics) of microfilled hybrid and nano dental composites
چکیده ندارد.
15 صفحه اولThe Effects of a Damage Arrestment Device on the Mechanical Behavior of Sandwich Composite Beams under Four-point Bending
The demand for an insert on composite sandwich structures to aid in the arrestment of face-core delamination is of great need. This research studies the use of a damage arrestment device (DAD) that connects the carbon fiber face sheets to the foam core to find whether an increase in the structural integrity of the sandwich beam results. Experimental analysis was employed to test the samples and...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials & Design
سال: 2019
ISSN: 0264-1275
DOI: 10.1016/j.matdes.2019.108112