Fatigue behaviour and fractography of extruded AZ80 magnesium alloys in very high cycle regime
نویسندگان
چکیده
منابع مشابه
Fatigue behaviour and fractography of extruded AZ80 magnesium alloys in very high cycle regime
In order to investigate the fatigue properties of extruded magnesium alloy in very high-cycle regime, rotary bending fatigue test was performed in ambient atmosphere at room temperature using the hourglass shaped specimens of AZ80 alloys extruded (Fspecimen) and treated by an artificial aging after extrusion (T5-specimen). From the experimental results, both specimens show a clear step-wise S-N...
متن کاملFATIGUE BEHAVIOUR OFA ROLLED AZ31 MAGNESIUM ALLOYS PREPARED BY EPAND BB CONDITIONS
Abstract: Rotating bending fatigue tests have been performed using smooth specimens of a rolled AZ31 magnesium alloy in laboratory air at ambient temperature. Fatigue strength and characteristic was evaluated and fracture mechanism was discussed on the basis fracture surface analysis. Electrical polishing (EP) as well as deep rolling (ball burnishing (BB)) U-notched specimens were performed on ...
متن کاملFatigue Performance of Laser Additive Manufactured Ti–6Al–4V in Very High Cycle Fatigue Regime up to 109 Cycles
Additive manufacturing technologies are in the process of establishing themselves as an alternative production technology to conventional manufacturing, such as casting or milling. Especially laser additive manufacturing (LAM) enables the production of metallic parts with mechanical properties comparable to conventionally manufactured components. Due to the high geometrical freedom in LAM, the ...
متن کاملCorrelation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys
* Corresponding author. Tel: 34 1 3944348; Fax: 34 1 3944357 E-mail: [email protected] ABSTRACT X-ray photoelectron spectroscopy (XPS) was used in order to investigate the correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys exposed to 98% relative humidity at 50oC. Commercially pure magnesium, used as the reference material, reveale...
متن کاملThe Effect of Environmental Parameters on the Corrosion Behavior of Simple Shear Extruded AZ91 Magnesium Alloys
In this study, the effects of forming method (extrusion) and environmental factors (solution pH and temperature) on the corrosion performance of AZ91 magnesium alloys were investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) and salt spray techniques. The polarization test results of the specimens showed that simple sh...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2010
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2010.03.020