Fatigue crack growth in a compressor stage of a turbofan engine by FEM-DBEM approach

A two-parameter model for crack growth simulation by combined FEM-DBEM approach

This paper describes the application of a two-parameters crack growth model, based on the usage of two threshold material parameters (DKth and Kmax,th) and on the allowance for residual stresses, introduced at the crack tip by a fatigue load spectrum or by material plastic deformations. The coupled usage of finite element method (FEM) and dual boundary element method (DBEM) is proposed in order...

Crack Propagation Calculations in Aircraft Engines by Coupled FEM-DBEM Approach

New generation jet engines are subject to severe reduced fuel consumption requirements. This usually leads to thin components in which damage issues such as thermomechanical fatigue, creep and crack propagation can be quite important. The combination of stresses due to centrifugal loads and thermal stresses usually leads to mixed-mode loading. Consequently, a suitable crack propagation tool mus...

Turbofan Engine Performance under Reliability Measures Approach

In this paper, the authors investigated the various factors, which can affect the performance of a turbofan engine. For this, the various subunits of a turbofan engine like inlet duct, compressor, combustion chamber, liner, turbine, exhaust nozzle etc. are investigated to find its various reliability characteristics through Markov process and supplementary variable technique (SVT). The main adv...

MSD crack propagation by DBEM on a repaired aeronautic panel

An Outrun Competition of Corrosion Fatigue and Stress Corrosion Cracking on Crack Initiation in a Compressor Blade

First row rotating blades of four axial-flow compressors were prematurely fractured. Previous investigations showed that the site atmosphere contains corrosive compounds which lead to an increase in possibility of pitting on the blades. It was also revealed that the crack was originated from two corrosion pits. Thus, this work is conducted to ascertain which of fatigue or stress corrosion crack...