Fatigue Crack Propagation in Welded Joints under Random Loading.
نویسندگان
چکیده
منابع مشابه
Fatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملFatigue Life Assessment of Welded Joints Considering Crack Propagation Based on Hot Spot Stress
In this study, fatigue test and crack propagation analysis of welded joints in ships and offshore structures were performed. The test models have two types of welded joints, T-joint and double plate. Test data is presented in S-N curves obtained by the Hot Spot Stress (HSS) approach. The S-N data for each length of crack were appraised to define the fatigue life of crack initiation and propagat...
متن کاملFatigue Behaviour of Al 6082-T6 Friction Stir Welded Tubular Joints under Torsional Loading
The aim of the present research is to investigate the fatigue behaviour of friction stir (FS) welded tubular joints in aluminium alloy subjected to torsional fatigue loading. To manufacture the samples which were tested, an MTS I-STIR process development system was equipped with a retracting tool specifically designed for these tubular welds. Al 6082-T6 FS welded samples were tested under cycli...
متن کاملUltra low cycle fatigue of welded steel joints under multiaxial loading
Ultra low cycle fatigue (ULCF) is a phenomenon that can be summarily defined as the deterioration of material properties under high amplitude cyclic loading, under which failure is reached typically within ten to twenty cycles. This phenomenon is observed in extreme loading scenarios such as earthquakes or exceptional winds where large cyclic strains are expected. Particularly sensitive are str...
متن کاملProbabilistic model for fatigue crack growth and fracture of welded joints in civil engineering structures
This paper presents a probabilistic assessment model for linear elastic fracture mechanics (LEFM). The model allows the determination of the failure probability of a structure subjected to fatigue loading. The distributions of the random variables for civil engineering structures are provided, and the relative importance of these random variables is determined. An example of a bridge detail is ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1991
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.40.1442