Fatigue Life Prediction for Bearing Steel Failed with Fish-Eye at Subsurface in Rotating Bending.
نویسندگان
چکیده
منابع مشابه
Assessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
Generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. The present paper investigates the effect of a notch on the fatigue life of the HSLA100 (high strength low alloy) steel which is widely applicable in the marine industry. Tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملassessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. the present paper investigates the effect of a notch on the fatigue life of the hsla100 (high strength low alloy) steel which is widely applicable in the marine industry. tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملBending Fatigue Failures in Valve Steel
In the present paper the effect of defects (viz. pits, gouges and oxide inclusions) will be reported. Although certain defects were uniformly distributed over the specimen surface, the majority of all fractures started in the edge region. An explanation to this behaviour is presented in terms of stress enhancement in the edge regions due to edge deflections.
متن کاملProbability Approach for Prediction of Pitting Corrosion Fatigue Life of Custom 450 Steel
In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...
متن کاملEnergy-Based Prediction of Low-Cycle Fatigue Life of CK45 Steel and SS316 Stainless Steel
In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2001
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.50.516