Fatigue Strength and Fracture Mechanism of Ceramic-Sprayed Steel.
نویسندگان
چکیده
منابع مشابه
Fatigue Fracture Strength of Implant-Supported Full Contour Zirconia and Metal Ceramic Fixed Partial Dentures
Objectives Zirconia restorations have been suggested as a more durable and more appealing alternative to metal restorations. However, their mechanical properties may be negatively affected by fatigue due to superficial stresses or low temperature degradation. This study aimed to assess the fatigue fracture strength of three-unit implant-supported full contour zirconia and pre-sintered cobalt-ch...
متن کاملFracture Strength of All-ceramic Restorations After
Fracture strength of monolithic and bilayered LAVA and e. max lower molar crowns after load cycling was measured and compared. The study included three groups (n = 8) from LAVA zirconia and three groups from e. max lithium disilicate to compare influences of different layers, thicknesses and manufacturing techniques. Prefabricated anatomically designed crowns were cemented to dies made from Z 1...
متن کاملInterior Fracture Mechanism Analysis and Fatigue Life Prediction of Surface-Hardened Gear Steel under Axial Loading
The interior defect-induced fracture of surface-hardened metallic materials in the long life region has become a key issue on engineering design. In the present study, the axial loading test with fully reversed condition was performed to examine the fatigue property of a surface-carburized low alloy gear steel in the long life region. Results show that this steel represents the duplex S-N (stre...
متن کاملFracture strength of teeth restored with ceramic inlays and overlays.
This study evaluated the fracture strength of teeth restored with bonded ceramic inlays and overlays compared to sound teeth. Thirty sound human maxillary premolars were assigned to 3 groups: 1- sound/unprepared (control); 2- inlays and 3- overlays. The inlay cavity design was Class II MOD preparation with an occlusal width of 1/2 of the intercuspal distance. The overlay cavity design was simil...
متن کاملFracture strength of ceramic bracket tie wings subjected to tension.
One of the most common areas of ceramic bracket fracture is within the tie-wing complex. When an archwire is ligated into position, tensile forces are placed under the tie wing. However, no study, to date, has focused specifically on the fracture resistance of the tie-wing complex. The aim of this study is to compare the tensile fracture strength of seven currently available ceramic brackets (I...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1993
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.59.1663