Fatigue Strength of Butt Welded Joints Having Angular Distortion
نویسندگان
چکیده
منابع مشابه
Improving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملResidual Stresses in Butt and Socket Welded Joints
A finite element scheme for simulation of welding residual stresses is presented in this paper. Detailed thermal and residual stress analyses for butt-welded and socket-welded pipes are performed using ANSYS and ABAQUS. The calculated distribution of axial stress and hoop stress at welded joint are validated against experimental results. Furthermore, residual stress relaxation under high amplit...
متن کاملA Study of Effect of Groove Angle on Angular Distortion and Impact Strength in Butt Welds
Welding is an area in which technological developments out match the developments in its science base, which is primarily driven by the phenomenal industrial demand for welded structure. Reliability, Reproducibility and Viability requirements are forcing Technologists to look at weld defects such as distortion, hot cracking, in a systematic and logical approach than on adhoc basis. Distortion i...
متن کاملThe Fatigue Strength of Fillet Welded Connections
This report describes a study of the fatigue behavior of fillet welded joints stressed perpendicular to the weld line. The study included an experimental phase in which the stiess-life and cracking behavior of load and nonload carrying fillet weld joints was determined. This experimental study concentrated on the fatigue behavior in the transition region between high and low cycle fatigue 3 5 (...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Naval Architects of Japan
سال: 1976
ISSN: 1884-2070,0514-8499
DOI: 10.2534/jjasnaoe1968.1976.140_259