First VAMAS USA interlaboratory comparison of high temperature superconductor critical current measurements
نویسندگان
چکیده
منابع مشابه
Interlaboratory Comparison on High-Temperature Superconductor Critical-Current Measurements
An extensive interlaboratory comparison was conducted on high temperature superconductor (HTS) critical-current measurements. This study was part of an international cooperative effort through the Versailles Project on Advanced Materials and Standards (VAMAS). The study involved six U.S. laboratories that are recognized leaders in the field of HTS. This paper includes the complete results from ...
متن کاملKiloampere, Variable-Temperature, Critical-Current Measurements of High-Field Superconductors
We review variable-temperature, transport critical-current (I c) measurements made on commercial superconductors over a range of critical currents from less than 0.1 A to about 1 kA. We have developed and used a number of systems to make these measurements over the last 15 years. Two exemplary variable-temperature systems with coil sample geometries will be described: a probe that is only varia...
متن کاملHigh critical-current superconductor-InAs nanowire-superconductor junctions.
We report on the fabrication of InAs nanowires coupled to superconducting leads with high critical current and widely tunable conductance. We implemented a double lift-off nanofabrication method to get very short nanowire devices with Ohmic contacts. We observe very high critical currents of up to 800 nA in a wire with a diameter of 80 nm. The current-voltage characteristics of longer and suspe...
متن کاملEnhanced critical current density in the pressure-induced magnetic state of the high-temperature superconductor FeSe
We investigate the relation of the critical current density (Jc) and the remarkably increased superconducting transition temperature (Tc) for the FeSe single crystals under pressures up to 2.43 GPa, where the Tc is increased by ~8 K/GPa. The critical current density corresponding to the free flux flow is monotonically enhanced by pressure which is due to the increase in Tc, whereas the depinnin...
متن کاملInterlaboratory Comparison of Magnetic Thin Film Measurements
A potential low magnetic moment standard reference material (SRM) was studied in an interlaboratory comparison. The mean and the standard deviation of the saturation moment m s, the remanent moment m r, and the intrinsic coercivity H c of nine samples were extracted from hysteresis-loop measurements. Samples were measured by thirteen laboratories using inductive-field loopers, vibrating-sample ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IEEE Transactions on Appiled Superconductivity
سال: 1995
ISSN: 1051-8223
DOI: 10.1109/77.402610