Formation and reversion of strain induced martensite on Fe-Cr-Ni alloys
نویسندگان
چکیده
منابع مشابه
The Effect of Nickel Increasing and Aluminum Addition on Sulfidation Resistance of Fe-Ni-Cr Alloys (TECHNICAL NOTE)
In this research the effects of; increasing the amount of nickel and adding aluminum to create and prolong sulfidation resistance of Fe-Ni-Cr alloys have been investigated. Sulfidation tests were carried out at 1100°C in S/O bearing atmosphere. Prior to the tests, the specimens were annealed in argon at 1250°C for 8 hrs. Weight changes were measured and corroded deposits were analyzed byscannin...
متن کاملThermally activated growth of lath martensite in Fe–Cr–Ni–Al stainless steel
The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...
متن کاملMicrostructural Examination of Ni-ion Irradiated Fe-Ni-Cr Alloys Followed to Micro-zone Deformation
Examination of deformation microstructures induced by micro-indentation technique by means of transmission electron microscopy following an MV range metallic ion irradiation was performed in order to study the influence of irradiation-produced microstructural defects on plastic deformation behavior of materials. In this work, specimens of an Fe-Cr-Ni austenitic model ternary alloy before and af...
متن کاملThermally activated growth of lath martensite in Fe- Cr-Ni-Al precipitation hardenable stainless steel
The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...
متن کاملThe Effect of Nitrogen on Martensite Formation in a Cr-Mn-Ni Stainless Steel
The influence of nitrogen (0 to 0.27 wtYo) on martensite formation in an experimental low-nickel stainless-steel alloy (Fe-17Cr-7Mn-4Ni) has been investigated. The alloys containing 0.1 wtYo or more nitrogen are fully austenitic at room temperature; those containing less nitrogen consist of a mixture of austenite, martensite and S-ferrite. The alloys containing less than 0.2 wtYo nitrogen are m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Rem: Revista Escola de Minas
سال: 2013
ISSN: 0370-4467
DOI: 10.1590/s0370-44672013000200013