Formation and Sintering of Alkoxy-derived Al2O3-TiO2 Composite Powders.

Sintering of a-Al2O3-seeded nanocrystalline g-Al2O3 powders

This paper demonstrates that seeding nanocrystalline transition alumina powders is a viable option for producing high quality, alumina-based ceramics. By using a-Al2O3 concentrations of 51.25 wt.% a-Al2O3 seed particles (equivalent to 5 10 seeds/cm of g-Al2O3) the sintering temperature is reduced from 1600 C for unseeded g-Al2O3 to 1300–1400 C in dry pressed powders. The scale of the sinteredmi...

Sintering Behaviors of Carbon Nanotubes—Aluminum Composite Powders

Carbon nanotubes (CNTs) are promising reinforcements for fabricating aluminum (Al) matrix composites with outstanding properties. The understanding of the consolidation process of CNT–Al composite powders plays a significant role in achieving high performances of bulk composites. In this study, an advanced consolidation technique of spark plasma sintering (SPS) was used to fabricate CNT–Al comp...

The Effect of Precursor Composition and Sintering Additives on the Formation of β-Sialon from Al, Si and Al2O3 Powders

A study was performed to investigate the effect of increasing the Al or Al2O3 precursor content, above the stoichiometric amount, on the formation of β-sialon by pressureless sintering of Al, Si and Al2O3 powders in flowing nitrogen gas. The effect of adding Y2O3 or Fe to the precursor mixture, on the β-sialon formation, was also studied. The phase morphology and yield produced by the various c...

SYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD

The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...

Sintering of Zircon Powders