Formation Mechanism of Strip Defects in Anodizing AA5252 Aluminium Alloy Sheets
نویسندگان
چکیده
منابع مشابه
Effects of temperature gradient magnitude on bending angle in laser forming process of aluminium alloy sheets
Laser forming is a thermal forming process which uses laser beam irradiation to produce the desired final forms. In this article, the effect of temperature gradient across Al 6061-T6 aluminum sheets on bending angle is studied. Input parameters including laser power, scan velocity, beam diameter, and sheet thickness are the effective process parameters which influence the temperature gradient....
متن کاملEffect of anodizing on pulsed Nd:YAG laser joining of polyethylene terephthalate (PET) and aluminium alloy (A5052)
A series of laser joining experiments between polyethylene terephthalate (PET) and aluminium alloy (A5052) were conducted to investigate the effect of anodizing on A5052 surface on dissimilar materials used in joining. In this study, PET/A5052 joints with anodized A5052 surface exhibited greater shear strength compared to PET/A5052 joints without anodizing. The shear strength of the joints was ...
متن کاملAnodizing of Magnesium Alloy Az31 by Alkaline Solution
-Anodizing of AZ 31 Mg alloy was investigate in 3M KOH solution for 10, 20 and 30min. at constant voltage of 5V. Atomic force microscope (AFM) used to investigate the roughness of anodic film formed on the surface while the scanning electron microscope (SEM) was used to determine the morphology of the anodic film, it was found that the roughness of the anodic film is mainly depend on the anodiz...
متن کاملImproved Technology for Hard Anodizing Dissolution of Aluminum Alloy Part
This paper deeply analyzes the main factors of the dissolved problems arising in the process of aluminum alloy hard anodizing, combined with the specific problems occurring in production practice, introduces in detail the method and thought to analyze and investigate the causes of dissolving, and puts forward targeted improvement technology. This paper is practically instructive and significant...
متن کاملPositron Lifetime Measurements of Subsurface Region in Aluminium Alloy and Aluminium Alloy Composite after Dry Sliding
This paper presents positron lifetime studies of the subsurface region of AK12 aluminium alloy and Al2O3-particle-reinforced AK12 aluminium alloy composite after sliding against steel in the pin-on-disc machine. The defect depth profile detected in the AK12 alloy extended up to 300 μm but for the composite AK12 the range of this profile was significantly shortened to less than ∼ 90 μm. The posi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2020
ISSN: 2261-236X
DOI: 10.1051/matecconf/202032604003