Grain fragmentation associated continuous dynamic recrystallization (CDRX) of hexagonal structure during uniaxial isothermal compression: High-temperature ? phase in TiAl alloys

Dynamic Recrystallization of the Constituent γ Phase and Mechanical Properties of Ti-43Al-9V-0.2Y Alloy Sheet

A crack-free Ti-43Al-9V-0.2Y alloy sheet was successfully fabricated via hot-pack rolling at 1200 °C. After hot-rolling, the β/γ lamellar microstructure of the as-forged TiAl alloy was completely converted into a homogeneous duplex microstructure with an average γ grain size of 10.5 μm. The dynamic recrystallization (DRX) of the γ phase was systematically investigated. A recrystallization fract...

Damage Behavior in Modern Automotive High Strength Dual Phase Steels During Uniaxial Tensile Deformation

In the present research, damage mechanisms during room temperature uniaxial tensile testing of two different modern high strength dual phase steels,DP780 and DP980, were studied. Detailed microstructural characterization of the strained and sectioned samples was performed by scanning electron microscopy (SEM). The results revealed that interface decohesion, especially at the triple junctions of...

Superplastic behaviour and mechanical properties of two phase TiAl alloys

High temperature plastic flow properties of two phase TiAl alloys containing 45 to 49 at.%Al have been investigated in thermo-mechanically grain refined materials in order to clarify the favourable microstructure and chemical composition for TiAl based superplastic materials. Grain sizes of thermomechanical treated materials and their grain size stability during subsequent high temperature defo...

Steady-State Grain Size in Dynamic Recrystallization of Minerals

Kinetics of Secondary Recrystallization in Grain-oriented Silicon Steel Studied by High-temperature Background

Secondary recrystallization id grain-oriented silicon steel is studied by the high-temperature background damping. Abnormal grain growth involves an abrupt drop of the background. The temperatures of initiation and completion of the secondary recrystallization are, thus, determined for the sane sample from the definite change in background with increasing temperature. The background measured on...