Grain refining by hot extrusion of AZ91D magnesium alloy machined chips and resulting high strain rate superplasticity
نویسندگان
چکیده
منابع مشابه
Grain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy
The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new interme...
متن کاملHot cracking in tungsten inert gas welding of magnesium alloy AZ91D
Plates of 3–5 mm in thickness were extracted from an AZ91D ingot and then butt joints of the plates were produced using tungsten inert gas (TIG) welding method. The TIG arc was also used to deposit welding beads on some of the thin plates. No cracking was found in the butt joints. However, hot cracking was always observed to propagate from the heat affected zone (HAZ) under the welding bead int...
متن کاملTensile and fatigue behavior of AZ91D magnesium alloy
Recently magnesium alloys, owing to their low density and excellent specific strength have been attractive to designers as an advanced material for coping with energy conservation and environmental pollution regulations. Much of the recent developments of magnesium alloys and processes have been driven by the requirements of the aerospace industry, although some successful ones have found appli...
متن کاملFracture Analysis of High Strain Rate Torsion Samples of Aluminium Zinc Magnesium Copper Alloy
All materials have been historically tested at static loading conditions. With the advent of technology, the study of behaviour of materials at high strain rate was done using various methods. The principle of split Hopkinson bar was used to study high strain rate of material in the range of 102s-1 to 103s-1. Split Hopkinson bars were designed for all three modes of deformation and extensively ...
متن کاملNumerical Analysis of Az61 Magnesium Alloy Extrusion Process by Modified Equal Channel Angular Extrusion (ecae) Method
T. Bajor, M. Krakowiak, P. Szota, Czestochowa University of Technology, Czestochowa, Poland The paper presents the results of numerical modelling of AZ61 magnesium alloy hot deformation using modified ECAE method. The temperature-velocity conditions were analysed using FEM. The extrusion process was realised using the die with modified angular channel containing horizontal contracting zone in t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 2007
ISSN: 0451-5994,1880-8018
DOI: 10.2464/jilm.57.391