Hardness, Young’s Modulus and Elastic Recovery in Magnetron Sputtered Amorphous AlMgB14 Films
نویسندگان
چکیده
منابع مشابه
Low-temperature magnetron sputter-deposition, hardness, and electrical resistivity of amorphous and crystalline alumina thin films
Aluminum oxide films were grown by reactive magnetron sputtering. In order to maintain a stable deposition process and high deposition rate, a pulsed direct current bias was applied to the aluminum target and the substrate. An external solenoid was used to form a magnetic trap between the target and the substrate. The influence of substrate temperature, substrate bias, and the magnetic trap on ...
متن کاملStructure and morphology of magnetron sputtered CoCr thin films
The growth characteristics of magnetron sputtered Co-22%Cr thin films on amorphous glass or carbon substrates have been investigated utilizing transmission electron microscopy, X-ray diffraction and electrical resistivity measurements. Results indicate that the initial deposit is “amorphous”. but that small crystallites form before the film reaches 5 nm film thickness. By 10 nm, well oriented g...
متن کاملFabrication and Characteristics of RF Magnetron Sputtered ITO Thin Films
Indium tin oxide (ITO) films have been deposited onto glass substrates by ifmagnetron sputtering without insitu substrate heating. The as-deposited films have an electrical resistivity of 5x1O a-cm, visible transmittance of about 85%, and infrared (IR) reflectance of above 80% at 5 jim. The effect of sputtering parameters on the deposition rate and the electrical and optical properties of ITO f...
متن کاملSelf-induced Crystallinity in RF Magnetron Sputtered ZnO Thin Films
ZnO films were coated on the order of micrometer thickness on various substrates using RF magnetron sputtering. Glass, mica and Si were used as amorphous and crystalline substrates to study film growth. X-ray diffraction measurements revealed a self-induced, (002) oriented texture on all substrates. Effects of residual stresses on growth behavior and possible mechanisms of textured crystallizat...
متن کامل349 R.f. Planar Magnetron Sputtered Zno Films I: Structural Properties
The structural properties of r.f. planar magnetron sputtered ZnO films are studied as a function of deposition parameters: substrate type, substrate temperature, sputter gas pressure, growth rate and sputtering power. These films are applied as piezoelectric transducers in micromechanical sensors and actuators. The electric properties, and consequently the piezoelectric behaviour, depend strong...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Crystals
سال: 2020
ISSN: 2073-4352
DOI: 10.3390/cryst10090823