High-pressure high-temperature synthesis and structure of α-tetragonal boron.
Microcrystals of α-tetragonal (α-t) boron with unit cell parameters a=9.05077(6) and c=5.13409(6) Å and measured density 2.16-2.22 g cm-3 were obtained by pyrolysis of decaborane B10H14 at pressures of 8-9 GPa and temperatures of 1100-1600 ○C. The crystal structure is in good agreement with the model proposed by Hoard et al (1958 J. Am. Chem. Soc.80 4507). However, compared to the original mode...
متن کاملHigh-pressure – High-temperature Synthesis of Na6MnO4
Z. Naturforsch. 2009, 64b, 487 – 490; received February 20, 2009 The title compound has been synthesized under 4 GPa and at 500 ◦C from Na2O and MnO as starting materials. Rietveld refinement of the X-ray powder pattern indicates that Na6MnO4 is isostructural to Na6ZnO4 and thus is representing the second manifestation of an “isolated” [MnO4]6− anion after Na14Mn2O9. The compound crystallizes i...
متن کاملconsequence analysis of the leakage, ignition and explosion during high pressure sour gas injection process to the oil reservoir
there is no doubt that human being needs to become integrated with industry and industry needs to be progressed, daily. on the other hand, serious events in industrial units specially in oil industries has been shown that such damages and events are industry related ones. the consequence of such events and damages which resulted in chemical and poisoned explosions and loss of life and property ...
High-pressure / High-temperature Synthesis of Transition Metal Oxide Perovskites
Perovskite and related Ruddlesden-Popper type transition metal oxides synthesised at high pressures and temperatures during the last decade are reviewed. More than 60 such new materials have been reported since 1995. Important developments have included perovskites with complex cation orderings on A and B sites, multiferroic bismuth-based perovskites, and new manganites showing colossal magneto...
متن کاملSynthesis of an orthorhombic high pressure boron phase.
The densest boron phase (2.52 g cm-3) was produced as a result of the synthesis under pressures above 9 GPa and temperatures up to ∼1800 °C. The x-ray powder diffraction pattern and the Raman spectra of the new material do not correspond to those of any known boron phases. A new high-pressure high-temperature boron phase was defined to have an orthorhombic symmetry (Pnnm (No. 58)) and 28 atoms ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Science and Technology of Advanced Materials
سال: 2011
ISSN: 1468-6996,1878-5514
DOI: 10.1088/069801