High-Temperature Corrosion Behaviour of Chromium Based Alloys for High Temperature SOFC
نویسندگان
چکیده
منابع مشابه
High-temperature Corrosion Behavior of Iron Aluminide Alloys and Coatings
A multi-year effort has been focused on optimizing the long-term oxidation performance of ingot-processed (IP) and oxide-dispersion strengthened (ODS) Fe3Al and iron aluminidebased coatings. Based on results from several composition iterations, a Hf-doped alloy (Fe28Al-2Cr-0.05at.%Hf) has been developed with significantly better high temperature oxidation resistance than other iron aluminides. ...
متن کاملChromium Deposition on Cobalt-Based Alloys by Pack-Cementation and Behaviour of the Coated Alloys in High Temperature Oxidation
Two TaC-strengthened cobalt-based alloys, with compositions Co-10Cr-0.25C-4.4Ta and Co-10Cr-0.5C-8.7Ta (wt.%) underwent Cr-deposition by pack-cementation, followed by heat-treatment to allow Cr diffusing deeper in their sub-surface. Thereafter they were tested for 50 hours at 1200°C in a thermobalance. These alloys were successfully enriched in chromium, with a maximal content on surface of abo...
متن کاملHigh Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملFundamental aspects of high-temperature corrosion
Some recent considerations in three widely different aspects of high-temperature corrosion are summarized: 1) reactions at the metavscale interface in support of scale growth; 2) mass transfer effects in the control of evaporation of volatile reaction products; and 3) the codeposition of multiple elements for diffusion coatings using halide-activated cementation packs. The climb of misfit edge ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ECS Proceedings Volumes
سال: 1997
ISSN: 0161-6374,2576-1579
DOI: 10.1149/199740.1306pv