Highly Stable Fluorine-Intercalated Graphite Fibers Coated with Graphite Fluoride Film
نویسندگان
چکیده
منابع مشابه
Ternary Intercalation Compound of Graphite with Aluminum Fluoride and Fluorine
A ternary intercalation compound of graphite with AIF3 and F2, CXF(A1F3)J/ was prepared under fluorine atmosphere at temperatures of 20-400 °C. The typical 1st stage compound has a composition of C6F(AlF3)o,i5 with a repeat distance of 940 pm. Rapid progress in the reaction led of the formation of graphite fluoride, (C2F),,. ESCA spectra indicate that the chemical bond between host graphite and...
متن کاملC60 Intercalated Graphite as Nanolubricants
We synthesized the novel nanocomposite consisting of alternately stacked single graphene sheets and a C60 monolayer by using the graphite intercalation technique in which alkylamine molecules help intercalate large C60 molecules into the graphite. It is found that the intercalated C60 molecules can rotate in between single graphene sheets by using 13C NMR measurements. The grease with the nanoc...
متن کاملSynthesis and Characterization of Highly Intercalated Graphite Bisulfate
Different chemical formulations for the synthesis of highly intercalated graphite bisulfate have been tested. In particular, nitric acid, potassium nitrate, potassium dichromate, potassium permanganate, sodium periodate, sodium chlorate, and hydrogen peroxide have been used in this synthesis scheme as the auxiliary reagent (oxidizing agent). In order to evaluate the presence of delamination, an...
متن کاملMicrostructural Characterization of Cobalt-Tungsten Coated Graphite Fibers
The present research concerns an electrodeposited cobalt-tungsten alloy coating on graphite fibers. Annealed and unannealed coated fibers were analyzed by scanning electron microscopy/energy dispersive x-ray spectroscopy (SEM/EDS), x-ray diffraction (XRD), and transmission electron microscopy (TEM). The mole fraction of tungsten in the as-deposited cobalt-tungsten coating was found to be (7.10 ...
متن کاملSupermetallic conductivity in bromine-intercalated graphite
Exposure of highly oriented pyrolytic graphite to bromine vapor gives rise to in-plane charge conductivities which increase monotonically with intercalation time toward values for 6 at % Br that are significantly higher than Cu at temperatures down to 5 K. Magnetotransport, optical reflectivity and magnetic susceptibility measurements confirm that the Br dopes the graphene sheets with holes whi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TANSO
سال: 1993
ISSN: 1884-5495,0371-5345
DOI: 10.7209/tanso.1993.148