Hot Corrosion Resistance of Laser-Sealed Thermal-Sprayed Cermet Coatings
نویسندگان
چکیده
منابع مشابه
Thermal Sprayed Coatings Used Against Corrosion and Corrosive Wear
Coatings have historically been developed to provide protection against corrosion and erosion that is to protect the material from chemical and physical interaction with its environment. Corrosion and wear problems are still of great relevance in a wide range of industrial applications and products as they result in the degradation and eventual failure of components and systems both in the proc...
متن کاملHot corrosion behavior of HVOF-sprayed CoNiCrAlYSi coatings in a sulphate environment
HVOF-sprayed CoNiCrAlYSi coatings were tested at 900 °C in a hot corrosion environment containing sodium-potassium sulphates. The HVOF spraying caused the typical splat-on-splat structure. The results after the hot corrosion testing showed that the corrosion preferentially occurred at the coating surface and the splat boundaries. The oxidation along the splat boundaries can isolate the splat fr...
متن کاملSolid Particle Erosion of Thermal Sprayed Coatings
Solid particle erosion is an important material degradation mechanism. Although various methods of coating are tried and used for protection against erosion, thermal sprayed coating for such purpose is the most widely used method. In this chapter, evolution of thermal sprayed coating, erosion testing methods, and erosive wear of thermal sprayed coatings are discussed extensively with emphasis o...
متن کاملCorrosion Protection of Metallic Waste Packages Using Thermal Sprayed Ceramic Coatings
Ceramic coated carbon steel coupons were corrosion tested in water with dissolved salts to simulate exposure to evaporation concentrated groundwater in an underground nuclear repository. Metallography revealed no corrosion at the ceramic metal interface of dense coatings, even though electrical measurements demonstrated that the coatings were slightly porous. Experimental results and a model to...
متن کاملPitted Corrosion Detection of Thermal Sprayed Metallic Coatings Using Fiber Bragg Grating Sensors
Metallic coatings using thermal spraying techniques are widely applied to structural steels to protect infrastructure against corrosion and improve durability of the associated structures for longer service life. The thermal sprayed metallic coatings consisting of various metals, although have higher corrosion resistance, will still corrode in a long run and may also subject to corrosion induce...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Coatings
سال: 2019
ISSN: 2079-6412
DOI: 10.3390/coatings9060347