Hot-Deformation Behavior and Microstructure Evolution of the Dual-Scale SiCp/A356 Composites Based on Optimal Hot-Processing Parameters

نویسندگان
چکیده

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effects of Carbon on the Microstructure and Hot Deformation Behavior

The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. &#10The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite r...

متن کامل

Effects of Carbon on the Microstructure and Hot Deformation Behavior

The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite reg...

متن کامل

effects of carbon on the microstructure and hot deformation behavior

the effects of carbon content on the dynamic and static softening mechanisms of ti microalloy steels were investigated both in ferrite and austenite regions. the results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. this is due to the ti(cn) and tic precipitates and also the free carbon content. in the ferrite regio...

متن کامل

Influence of Initial Microstructure on Hot Deformation Behavior of Duplex Stainless Steels

In this research the effect of initial microstructure on hot deformation behavior in terms of Ferrite-to-Austenite ratios is studied. Two types of stainless steels C1 and C2 were homogenizing heat-treated and deformed under hot compression examinations at temperatures 900ºC and 1100ºC at strain rate of 0.1s-1. The results showed that the flow stress levels of specimens are strongly r...

متن کامل

Investigation on Hot Deformation Behavior and Hot Processing Map of BSTMUF601 Super-Alloy

Abstract: Isothermal compression tests of BSTMUF601 super-alloy in the temperature range of 950 ̋C–1200 ̋C and at the strain rates of 0.2 s ́1, 5 s ́1, 10 s ́1 were performed on a Gleeble-1500D thermo-mechanical simulator. Based on the hyperbolic sine function, the unified constitutive equations and hot processing maps during the hot deformation process were established. The flow stress predicted by...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Materials

سال: 2020

ISSN: 1996-1944

DOI: 10.3390/ma13122825