Hot-Deformation Behavior and Microstructure Evolution of the Dual-Scale SiCp/A356 Composites Based on Optimal Hot-Processing Parameters
نویسندگان
چکیده
منابع مشابه
Effects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. 
The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite r...
متن کاملEffects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite reg...
متن کاملeffects of carbon on the microstructure and hot deformation behavior
the effects of carbon content on the dynamic and static softening mechanisms of ti microalloy steels were investigated both in ferrite and austenite regions. the results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. this is due to the ti(cn) and tic precipitates and also the free carbon content. in the ferrite regio...
متن کاملInfluence of Initial Microstructure on Hot Deformation Behavior of Duplex Stainless Steels
In this research the effect of initial microstructure on hot deformation behavior in terms of Ferrite-to-Austenite ratios is studied. Two types of stainless steels C1 and C2 were homogenizing heat-treated and deformed under hot compression examinations at temperatures 900ºC and 1100ºC at strain rate of 0.1s-1. The results showed that the flow stress levels of specimens are strongly r...
متن کاملInvestigation on Hot Deformation Behavior and Hot Processing Map of BSTMUF601 Super-Alloy
Abstract: Isothermal compression tests of BSTMUF601 super-alloy in the temperature range of 950 ̋C–1200 ̋C and at the strain rates of 0.2 s ́1, 5 s ́1, 10 s ́1 were performed on a Gleeble-1500D thermo-mechanical simulator. Based on the hyperbolic sine function, the unified constitutive equations and hot processing maps during the hot deformation process were established. The flow stress predicted by...