Hydrogen Dissolution and Structural Changes in Electrodeposited Cr Films*
Effects of hydrogen on the structure of electrodeposited Cr films have been investigated by combining X-ray diffraction and thermal desorption spectroscopy, systematically varying the plating conditions. A large amount of hydrogen was dissolved at high current densities in a Cr-rich bath at low temperatures, and caused structural changes from bcc to hcp and fcc hydrides with increasing hydrogen...
متن کاملHydrogen Diffusion and Trapping in Electrodeposited Nickel
In an attempt to quantify grain boundary diffusion of hydrogen in nickel, permeation in electrodeposited foil has been investigated. Pinhole-free specimens were plated from a nickel sulfamate bath onto a reusable anodized titanium cathode. The microstructure was a mixture of regions of fine grains (diameters <0.1 tm) and individual grains up to 2 tm in diameter. The specimens were subjected to ...
متن کاملInvestigation of Tribological Behavior of Electrodeposited Cr, Co-Cr and Co-Cr/TiO2 Nano-Composite Coatings
Electrodeposition is a simple and economic technique for precision coating of different shaped substrates with pure metal, alloy or composite films. Dc electrodeposition was used to produce Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III) based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles concentration on co-deposition of these particles along with Cr con...
متن کاملThickness induced structural changes in polystyrene films.
Changes to the structure of polystyrene melt films as measured through the spectrum of density fluctuations have been observed as a function of film thickness down to the polymer radius of gyration (Rg). Films thicker than 4Rg show bulklike density fluctuations. Thinner films exhibit a peak in S(q) near q=0 which grows with decreasing thickness. This peak is attributed to a decreased interpenet...
متن کاملProperties of Electrodeposited WO3 Thin Films
Galvanostatic electrodeposition was used to produce transparent and amorphous WO3 films that showed color changes from clear to blue in response to the applied potential of ±1.0 V. The 61% in transmittance variation was measured at wavelength of 633 nm. The roughness of 16.7 nm was obtained by atomic force microscopy (AFM). The scanning electron microscopy (SEM) evidenced homogeneous morphology...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2005
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.46.963