Hydrometallurgical Recovery of Metals from Large Printed Circuit Board Pieces
نویسندگان
چکیده
منابع مشابه
Hydrometallurgical Recovery of Metals from Large Printed Circuit Board Pieces
The recovery of precious metals from waste printed circuit boards (PCBs) is an effective recycling process. This paper presents a promising hydrometallurgical process to recover precious metals from waste PCBs. To simplify the metal leaching process, large pieces of PCBs were used instead of a pulverized sample. The chemical coating present on the PCBs was removed by sodium hydroxide (NaOH) tre...
متن کاملMetals Content in Printed Circuit Board Waste
This paper an presents analysis of metals in waste of printed circuit boards (PCB) covering types of PCB, segregated from PC computers, mobile phones, and mixed. The presented data identifies metals and other substances found in PCB waste based on elemental and technical analysis of PCBs. PCB categorization based on gold concentration is presented, resulting in two groups: electric and electron...
متن کاملRecovery of Heavy Metals from Spent Etching Waste Solution of Printed Circuit Board (PCB) Manufacturing
The process of etching is the most crucial part of the work of manufacturing printed circuit boards (PCB). In the etching process by nitric acid, a spent etching waste solution of composition 250 g/L HNO3, 30-40 g/L Cu, 30-40 g/L Sn, 30-40 g/L Pb and 20-25 g/L Fe is produced. High metal concentrations in the spent etching waste solution make it a viable candidate for the recovery of metals. Rec...
متن کاملRecovery of high purity precious metals from printed circuit boards.
Waste printed circuit boards (WPCB) have an inherent value because of the precious metal content. For an effective recycling of WPCB, it is essential to recover the precious metals. This paper reports a promising method to recover the precious metals. Aqua regia was used as a leachant and the ratio between metals and leachant was fixed at 1/20 (g/ml). Silver is relatively stable so the amount o...
متن کاملLeaching studies for metals recovery from printed circuit boards scrap
In this paper, the leaching behavior of the major metals present in printed circuit boards waste is evaluated, aiming at its recycling by hydrometallurgy. Several leachants were compared (sulfuric, hydrochloric and nitric acids, at 2 M H concentration), at temperatures of 25oC and 90oC and 4 hours of reaction time. Sulfuric acid leaching was not very promising concerning metals dissolution bein...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2015
ISSN: 2045-2322
DOI: 10.1038/srep14574