<I>In Situ</I> Formation and Refinement of Mg<SUB>2</SUB>Si in Fiber-Reinforced AZ91D Magnesium Alloy
نویسندگان
چکیده
منابع مشابه
In Situ Formation and Refinement of Mg2Si in Fiber-Reinforced AZ91D Magnesium Alloy*
In order to obtain a lightweight material having an excellent high-temperature strength, Mg alloy composites reinforced with short alumina fibers and in situ Mg2Si particles were fabricated. The composites were fabricated by pressureless infiltration of the Mg alloy melt into the preform consisting of the fibers and attached Si particles. The volume fraction of Si particles in the preform, the ...
متن کاملHigh Temperature Properties of AZ91D Magnesium Alloy Composite Reinforced with Short Alumina Fiber and Mg_{2}Si Particle
Short alumina fiberand in situ Mg2Si particle reinforced magnesium alloy composites were fabricated by squeeze casting. The in situ Mg2Si particles were formed during the infiltration with the melt into the preforms consisting of the fibers having Si particles attached to their surfaces. The microstructure of the composites and their tensile strength and Young’s modulus in the range from 293K t...
متن کاملTensile and fatigue behavior of AZ91D magnesium alloy
Recently magnesium alloys, owing to their low density and excellent specific strength have been attractive to designers as an advanced material for coping with energy conservation and environmental pollution regulations. Much of the recent developments of magnesium alloys and processes have been driven by the requirements of the aerospace industry, although some successful ones have found appli...
متن کاملGrain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy
The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new interme...
متن کاملEffect of heat treatment on corrosion and electrochemical behaviour of AZ91D magnesium alloy
An AZ91D ingot in the as-cast condition was homogenized by solution treatment and then aged for various periods of time. The microstructures produced were studied in detail and the b phase volume fraction was measured quantitatively. The Corrosion resistance of all the different microstructures was studied in 3.5% NaCl solution through weight loss measurement in constant immersion conditions an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2007
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.f-mra2007834