A core-shell particle was fabricated by grafting amino-terminated hyperbranched polymer to the surface of silica nanoparticles. The influences of core-shell particle contents on the tensile and impact strength of the epoxy thermosets modified with amino-terminated hyperbranched polymer were discussed in detail. For comparison, core-shell particle was added into the epoxy/polyamide system for to...
متن کاملSurfactant Removal from Mesoporous Silica Shell of Core-Shell Magnetic Microspheres by Modified Supercritical CO2
In this paper, a kind of core–shell magnetic mesoporous microspheres of Fe3O4@SiO2@meso-SiO2 with high surface areawas prepared, where magnetic Fe3O4 nanospheres were used as the inner core, tetraethyl orthosilicate (TEOS) as silica source, and cetyltrimethylamonium bromide (CTAB) as pore forming agent. Methanol-enhanced s...
متن کاملStudy of Hyperbranched Poly(ethyleneimine) Polymers of Different Molecular Weight and Their Interaction with Epoxy Resin
Two different commercial hyperbranched poly(ethyleneimine)s (HBPEI), with molecular weights (MW) of 800 and 25,000 g/mol, and denoted as PEI800 and PEI25000, respectively, as well as the mixtures with a Diglycidyl Ether of Bisphenol-A (DGEBA) epoxy resin, have been studied using thermal analysis techniques (DSC, TGA), dielectric relaxation spectroscopy (DRS), and dynamic mechanical analysis (DM...
متن کاملExperimental data on the properties of polymer-modified cement grouts using epoxy and acrylic resin emulsions
The use of additives to improve the quality of cement grouts is crucial for civil engineering, especially in foundation construction. This article presents experimental data concerning the compressive strength, elastic modulus, bleeding and injectability of microfine cement grouts modified with epoxy and acrylic resin emulsions. Strength properties were obtained at different curing ages. For fu...
متن کاملNovel Organically Modified Core-Shell Clay for Epoxy Composites—“SOBM Filler 1”
Preparation of a novel organically modified clay from spent oil base drilling mud (SOBM) that could serve as core-shell clay filler for polymers is herein reported. Due to the hydrophilic nature of clay, its compatibility with polymer matrix was made possible through modification of the surface of the core clay sample with 3-aminopropyltriethoxysilane (3-APTES) compound prior to its use. Fourie...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Polymers
سال: 2017
ISSN: 2073-4360
DOI: 10.3390/polym9120684