Improved semiconducting CuO/CuFe2O4 nanostructured thin films for CO2 gas sensing
نویسندگان
چکیده
منابع مشابه
Fabrication, characterization and investigation of gas sensing properties of MoO3 thin films
In this research, molybdenum oxide (α-MoO3) thin films were coated on glass substrates using spray pyrolysis technique. 0.05 M ammonium heptamolybdate tetrahydrate was used as precursor and deionized water as solvent. The effects of carrier gas pressure, during the spraying of the solution, on the structural, optical, morphological and gas sensing properties of thin films were studied. X-ray di...
متن کاملGas Sensing Properties of Epitaxial LaBaCo2O5.5+δ Thin Films
Chemical reactivity and stability of highly epitaxial mixed-conductive LaBaCo2O5.5+δ (LBCO) thin films on (001) LaAlO3 (LAO) single-crystalline substrates, fabricated by using pulsed laser deposition system, were systematically investigated. Microstructure studies from x-ray diffraction indicate that the films are c-axis oriented with the interface relationship of [100]LBCO//[100]LAO and (001)L...
متن کاملAmmonia gas sensing property of nanocrystalline Cu2S thin films
Nanocrystalline semiconducting thin films of copper sulphide (Cu2S) were deposited by novel chemical route using aqueous solution of 0.1 M copper chloride, 0.05 M thiourea, complexing agent 10% aqueous ammonia (NH3) and hydrazine hydrate. The characterization and gas sensitivity of as deposited Cu2S thin film sensor have been investigated. The as deposited Cu2S thin films were observed to be ve...
متن کاملStudies on sol-gel dip-coated nanostructured ZnO thin films
Nanostructured ZnO thin films were prepared by sol-gel dip coating technique. Zinc acetate and ammonium hydroxide were used as precursors and ethanol was as solvent. Ammonium hydroxide (NH4OH) solution was added drop-wise under vigorous stirring to obtain the sol-gel of different pH (varying from 6.9 to 7.2). ZnO thin films were obtained by dipping the glass substrates for few seconds and then ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Sensors and Actuators B: Chemical
سال: 2014
ISSN: 0925-4005
DOI: 10.1016/j.snb.2014.07.088