Improvement of protective coating on Nd–Fe–B magnet by pulse nickel plating
نویسندگان
چکیده
منابع مشابه
Pulse reverse plating for uniform nickel height in zone plates
Nickel soft x-ray zone plates are fabricated by through-mask electroplating. The authors report on how a uniform nickel thickness can be obtained over the entire zone plate using pulse and pulse reverse plating. If the plating is carried out at a constant current the nickel thickness has been observed to decrease with radius. This results in lower outer zones and reduced diffraction efficiency ...
متن کاملNickel Plating and Electroforming
The material presented in this publication has been prepared for the general information of the reader and should not be used or relied on for specific applications without first securing competent advice. The Nickel Development Institute, its members, staff and consultants do not represent or warrant its suitability for any general or specific use and assume no liability or responsibility of a...
متن کاملElectroless Nickel Plating on Magnesium Alloy
he inherent lightness and good strength-to-weight ratio of T magnesium has focused attention on increasing applications in aerospace and allied fields. Its density is two thirds that of aluminum-a conventional structure material for aerospace. Magnesium has one drawback: It is prone to atmospheric corrosion. Further, because of its high chemical affinity for aqueous solutions, it is categorized...
متن کاملA new structure of Nd1+εFe4BB4 phase in NdFeB magnet
Sintered NdFeB magnets are relatively complex multiphase systems containing Nd2Fe14B matrix and about 15% of other intermetallics such as Nd1+εFe4BB4, Nd-oxides (Nd-rich phase), etc. Boron rich Nd1+εFe4B4 B forms in irregularly distributed heavily faulted grains of roughly the same size as those of the Nd2Fe14B phase [1]. The Curie temperature of this phase is 13K and, therefore, it is not ferr...
متن کاملElectroless Nickel Plating with Hypophosphite
In the previous chapter, the components of electroless nickel plating baths were discussed from the viewpoint of the function each performs in the bath, with little attention paid to their effect on the plating process. The metal and the electron source (the reducing agent) are consumed in the electroless plating reaction and so their concentrations in the bath are continuously decreasing. Ther...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Applied Physics
سال: 1998
ISSN: 0021-8979,1089-7550
DOI: 10.1063/1.367921