IMPROVING THE FORMABILITY OF STAINLESS STEEL 321 THROUGH MULTISTEP DEFORMATION FOR HYDROFORMING APPLICATIONS
نویسندگان
چکیده
منابع مشابه
The Strain Dependence of Post-Deformation Softening during the Hot Deformation of 304H Stainless Steel
Experiments were carried out in which the dependence of the fractional softening on temperature, time and strain rate was determined in a 304H stainless steel. Three prestrain ranges were identified pertaining to three different post-deformation softening behaviors: 1) prestraining to below the DRX critical strain: strongly strain dependent softening by SRX alone with softening kinetics control...
متن کاملmodification of nanoclay for improving the physico-mechanical properties of dental adhesives
هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...
The Electrochemical Behavior of AISI 321 Stainless Steel in Alkaline Media
In this paper, the electrochemical behaviour of passive films formed on AISI 321 stainless steel (AISI 321) immersed in 0.1 M NaOH + 0.1 M KOH solution was evaluated by different electrochemical techniques. For this purpose, passive films were formed at open circuit potential for 1 to 12 hours and then electrochemical measurements were done. The polarization curves suggested that AISI 321 showe...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملHot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Canadian Society for Mechanical Engineering
سال: 2013
ISSN: 0315-8977
DOI: 10.1139/tcsme-2013-0003