The effects of chemical composition variations on microstructure and mechanical properties of nanostructured, low temperature bainitic steels
Bainitic transformation at low transformation temperatures leads to a microstructure involving fine plates of bainitic ferrite and thin films of retained austenite. This microstructure has shown ultimate tensile strength of about 2.2 GPa, noticeable uniform elongation in the range of 5 to 30%, hardness values of about 600 to 670 HV and impact toughness in the range of 30 to 40 MPa m1/2. With ca...
متن کاملEffect of Mo Content on Microstructure and Property of Low-Carbon Bainitic Steels
In this work, three low-carbon bainitic steels, with different Mo contents, were designed to investigate the effects of Mo addition on microstructure and mechanical properties. Two-step cooling, i.e., initial accelerated cooling and subsequent slow cooling, was used to obtain the desired bainite microstructure. The results show that the product of strength and elongation first increases and the...
متن کاملAir cooled bainitic steels for strong, seamless pipes Part 2 – properties and microstructure of rolled material
In the first part of the present study, two steels were designed with the aim of achieving properties consistent with the specifications for the manufacture of seamless pipes. The alloys were intended to develop into mixtures of bainitic ferrite and carbon enriched retained austenite during cooling to ambient temperature from the pipe forming operations, thus avoiding the need for subsequent he...
متن کاملthe effects of chemical composition variations on microstructure and mechanical properties of nanostructured, low temperature bainitic steels
bainitic transformation at low transformation temperatures leads to a microstructure involving fine plates of bainitic ferrite and thin films of retained austenite. this microstructure has shown ultimate tensile strength of about 2.2 gpa, noticeable uniform elongation in the range of 5 to 30%, hardness values of about 600 to 670 hv and impact toughness in the range of 30 to 40 mpa m1/2. with ca...
متن کاملinvestigation of the electronic properties of carbon and iii-v nanotubes
boron nitride semiconducting zigzag swcnt, $b_{cb}$$n_{cn}$$c_{1-cb-cn}$, as a potential candidate for making nanoelectronic devices was examined. in contrast to the previous dft calculations, wherein just one boron and nitrogen doping configuration have been considered, here for the average over all possible configurations, density of states (dos) was calculated in terms of boron and nitrogen ...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Sciences
سال: 2020
ISSN: 2076-3417
DOI: 10.3390/app10010344