Influence of Coating Process on High-Temperature Oxidation Property for Plasma Sprayed Thermal Barrier Coating Systems
نویسندگان
چکیده
منابع مشابه
High-temperature degradation of plasma sprayed thermal barrier coating systems
Thermal barrier coating systems (TBCs) are used in gas turbines to prevent high-temperature degradation of metallic materials in the combustor and turbine. One of the main concerns regarding TBCs is poor reliability, and accurate life prediction models are necessary in order to fully utilise the beneficial effects of TBCs. This research project aims at developing deeper understanding of the deg...
متن کاملGraphene Oxidation Barrier Coating
Since its experimental isolation in 2004, graphene has shown some outstanding properties. We propose that graphene can be used as an oxidation barrier coating and its oxidation resistance weakens at the graphene grain boundaries. Copper is a superior conductor but is easily oxidized in air at room temperature or higher. Using graphene as a coating material may reduce the cost of protecting agai...
متن کاملInfluence on Thermal Barrier Coating Delamination Behaviour of Edge Geometry
Ceramic thermal barrier coatings are commonly used in gas turbine hot components (e.g., combustor liners/buckets and guide vane platforms). In components that are only partially coated or have cooling-air outlets, coating-end stress singularities may lead to the spallation of the coating. Depending on the geometry of the transition from coated to uncoated material, the severity of the stress si...
متن کاملCrack propagation in thermal barrier coating systems
Thermal barrier coating systems are used on top of highly stressed components in gas turbines to protect the nickel-based substrates. A well-established thermal barrier coating system consist of the bond-coat (BC) and the thermal barrier coating (TBC). A third layer is grown during service: the thermally grown oxide (TGO) between the BC and the TBC. The coatings fail in service because of diffe...
متن کاملThermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
The effects of the bond coat species on the delamination or fracture behavior in thermal barrier coatings (TBCs) was investigated using the yclic thermal fatigue and thermal-shock tests. The interface microstructures of each TBC showed a good condition without cracking or delamination after flame thermal fatigue (FTF) for 1429 cycles. The TBC with the bond coat prepared by the air-plasma spray ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals
سال: 2004
ISSN: 0021-4876
DOI: 10.2320/jinstmet.68.438