Influence of Steel Surface Property on Galvannealing Rate of Galvanized Steel Sheet
نویسندگان
چکیده
منابع مشابه
Corrosion of Galvanized Steel in Soils
The results of measurements of the corrosion of galvanized steel and of bare steel and zinc as reference materials after exposure to different soil conditions for a maximum of 13 years are reported. The magnitude and progress of corrosion of galvanized steel as determined by weight loss and pitting is interpreted in terms of the environmental conditions to which the specimens were exposed. From...
متن کاملInfluence of Substrate Molybdenum on Galvannealing Kinetics of an Advanced High Strength Steel
Advanced high strength steels (AHSS) are used for car body applications in the automotive industry to improve passenger safety, improve fuel efficiency and to lower harmful carbon emissions. Galvannealed AHSS are used to provide corrosion protection. AHSS are alloyed with several elements such as Mn, Si, Al, P, Mo, etc. to achieve better mechanical properties. However, the knowledge of the effe...
متن کاملThe Influence of Surface Roughness of Drawbead on Non-Symmetry Deep Drawing Cold Rolled Steel Sheet
This study was aimed to explain the influence of surface roughness of the drawbead on non-symmetry deep drawing cold rolled steel sheet to improve the drawability of cold rolled steel sheet. The variables used in this study included semi-circle drawbead with 3 levels of surface roughness which are 6.127 μm Ra, 0.963 μm Ra and 0.152 μm Ra and cold rolled steel sheet according to 3 grades of the ...
متن کاملStudies on defects in galvanized coating on steel wire
Causes for deposition of defective galvanized coating (lumpy deposition of coating during hot dip galvanizing) of carbon-steel wire have been investigated. It is established that the lumpy deposition is caused due to segregation of silicon on the surface of steel wire. Due to this change in composition of the steel at surface, the regions get modified and lie in Sandelin hyper reactive zone. Th...
متن کاملDetermination of Surface Topography and Composition of Cr-Free Pretreatment Layers on Hot Dip Galvanized Steel
Topography and composition of Cr-free, titanium-based pretreatment layers on hot dip galvanized steel were studied with scanning electron microscopy, atomic force microscopy, time of flight secondary ion mass spectrometry and Auger electron spectroscopy. A layer within the target coating weight range (4-10 mg Ti/m) for industrial coil coating processes contained a micro-structure with hillocks ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 2003
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.89.1_23