Influence of sulfate-reducing bacteria on the biocorrosion of mild steel coated with hybrid polyetherimide-ZnO or CuO bilayer composites

Mild steel (MS) coated with protective bilayer hybrid coatings of polyetherimide, and ZnO/CuO was exposed to artificial treated wastewater (ATWW) inoculated Desulfovibrio sp. (biotic system). Proteins from the extracellular polymeric substances (EPS) matrix responded coatings. PEI-CuO offered highest performance against biocorrosion. The higher resistivity value 2.17×10 6 Ω·cm 2 contrasted decrease 1.5×10 5 1.6×10 3 for PEI-ZnO PEI coatings, respectively. one order magnitude increased resistance biotic system, compared sterilized ATWW (abiotic system), resulted nature bacterial biofilm. Supplementary Materials: material this article is supplied as a separate file: crchim-227-suppl.pdf L’acier doux recouvert de revêtements hybrides bicouches protecteurs polyétherimide et été exposé à des eaux usées artificielles inoculées par (système biotique). Les protéines la matrice polymères extracellulaires ont réagi aux revêtements. Le offert les meilleures performances contre La valeur résistivité plus élevée 2,17×10 contraste avec diminution respectivement 1,5×10 1,6×10 pour PEI. résistance accrue d’un ordre grandeur du système biotique, rapport l’ATWW stérilisé abiotique), résulte protectrice biofilm bactérien. Compléments : Des compléments sont fournis cet dans le fichier séparé