INTENSIFICATION OF THE SINTERING PROCESS OF CERAMIC MATERIALS BASED ON THE BaO – Al2O3 – SiO 2 SYSTEM

The article examines the effect of additives on intensification sintering process ceramic materials based BaO – Al2O3 SiO2 system. Taking into account different mechanisms interaction with main matrix, modifiers MgO, Cr2O3, ZrSiO4, TiO2 and mineralizers CaCO3, B2O3, MoO3, SnO2 : Li2O were selected for research. On basis conducted complex studies, it was established that most promising intensifier celsian is eutectic additive in amount 1 wt.% following characteristics: water absorption 5.1%, porosity 13.4%, apparent density 2.62 g/cm3. results X-ray phase analysis show synthesis reaction complete at a temperature 1200 °С, which confirmation decrease by 100 °С. obtained ceramics meet requirements radio-transparent can be used manufacture individual parts aerospace industry.