Interface layer deformation thickening analysis of hot rolling carbon steel–stainless steel clad plate
نویسندگان
چکیده
منابع مشابه
A Roll Wear Prediction Model in Hot Plate Rolling
In this paper, the wear of work roll in hot plate rolling is introduced and the parameters affecting wear mechanisms in hot strip mill are investigated. In addition, different wear mechanisms in hot rolling and the differences between these mechanisms in different stands are explained. Using the finite element method and the rolling equations, a work roll wear model is proposed. Wear is modeled...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملPrediction of Deformation Resistance of Low Carbon Steels during Hot Rolling
Phenomenological approach to the description of deformation resistance behaviour of steel and its microstructure development under the service hot rolling condition is still the most common useful and powerful. Utilising different experimental equipment such as torsion plastometer [1-5], compression plastometer [6-9], or advanced laboratory mills [10, 11] as well as different deformation techni...
متن کاملHot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملEffects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. 
The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite r...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2020
ISSN: 2053-1591
DOI: 10.1088/2053-1591/ab6c91